Feature:
This product is one kind of sulfur silicone sealant with one acid component which could be applied at any climate and could take chemical reaction with the water in air rapidly. Good aging-resistant ability, high flexible, perfect performance of high or low temperature resistant. Several machine waster water resistant, good elastic. Color: transparent, black, grey, blue, red.
Scope of application:
This product is used for sealing of car, gear case of motor, fore-and-art board, water pump, plane flange, cover board of other machine equipment.
Using Method:
1. Cleaning up the surface with the cotton fabric, guarantees the surface not to have the dust, the greasy dirt.
2. Pierce the seal with the cap, cover the mouth, wrap the nozzle, cut bevel the size needed.
3. The operation should be continuously
4. After operated for 10 minutes, reassembly the parts.
Warning:
1. The working environment should be clean, dry and ventilate.
2. Finish operation within 1 hour for the cleaned material，otherwise must clean again. If the cleaned surface exposes in the rain water or the contamination, also must re-clean.
3. Avoid eye contact before solidification, if touches the eye carelessly, use massive water to wash, if serious go to see a doctor, if touches the skin, wipe off by dry clothes or tissue.
4. When operation, must hold the glue steadily, cannot separate, guards against mixes in the air and form bubble , affects the seal effect.
5. After operation, take off the cap mouth immediately, close the packing cover tightly to prevent the moisture enter and cause solidification. Wipe off the glue left at glue mouth..
6. Do not put into mouth and keep reach out of kids.
Storage and packing:
1. This product is non-flammable，seal store in 10-27℃ cool dry place, term of validity for top grade, medium grade, is 12 months, 9 months respectively.
2. Packing：110g/pc. 70g/pc，in plastic tube
Technical Feature:
|
No
|
Item
|
Technical Parameter
|
|
Top grade
|
Common grade
|
|
1
|
Prolapse distance
|
Vertical ， mm
|
≤ 3
|
|
Aclinic
|
No distortion
|
|
2
|
Density
|
1.34-1.42
|
1.34-1.42
|
|
3
|
Thickness
|
8.6-9.2
|
9.0-9.6
|
|
4
|
Extrusion rate ， ml/min
|
≥ 400
|
≥ 400
|
|
5
|
Surface dry time,mm
|
30-120
|
30-90
|
|
6
|
Shao's hardness
|
40-60
|
40-60
|
|
7
|
Extend rate/MPa
|
2 3 ℃ Standard
|
≥ 0.6
|
≥ 0.5
|
|
Under water
|
≥ 0.45
|
/
|
|
Water-Ultraviolet radiaton
|
≥ 0.45
|
/
|
|
8
|
Standard condition bonding
destroy area %
|
≤ 5
|
≤ 10
|
|
9
|
Under water bonding destroy
area%
|
≤ 5
|
/
|
|
10
|
Water-Ultraviolet radiation
destroy area %
|
≤ 5
|
/
|
|
11
|
Elastic recover rate %
|
≥ 90
|
≥ 80
|
|
12
|
Extend bonding rate
|
100% no damage
|
60% no damage
|
|
13
|
Hot aging
|
Quality damage
rate%
|
≤ 8
|
≤ 15
|
|
Chap 、 pulverization
|
No
|
No
|
|
14
|
Solidify speed mm/24h
|
2-8
|
|
15
|
Using temperature
|
-40~ 15 0 ℃
|
-40~ 12 0 ℃
|
|